About Polycarbonate

Best Sale

Shutter Multiwall Polycarbonate Sheet

Shutter Multiwall Polycarbonate Sheet

It is new generation structural design of Multiwall Sheet, which is with multi concept of shutters and anti-UV.

أكثر من
IR Absorbent Polycarbonate Sheet

IR Absorbent Polycarbonate Sheet

It is added infrared absorber to block heat and also offers advantages in impact, light transmission, and UV stability.

أكثر من

Polycarbonate Sheet Manufacturer & Supplier- SUN ASIA

Based in Taiwan, Sun Asia Enterprise Co., Ltd. is one of the primary polycarbonate sheet suppliers since 1990. Multiwall polycarbonate sheets, solid polycarbonate sheets, frosted polycarbonate sheets with other wide range of polycarbonate sheet solutions for traditional construction, civil engineering, interior design and lighting industries.

SUN ASIA polycarbonate sheets are outstanding for impact strength and high temperature resistance. As well as excellent transparency and surface brightness, good chemical resistance, recyclable and safe.

With both advanced polycarbonate sheet technology and 29 years of experience, SUN ASIA makes sure to meet each customer's demands.

About Polycarbonate


Properties of Polycarbonate

1. Property of Heat:
  • Temperature of Heat deformation: The temperature that causes Polycarbonate panels to deform is 130°C, and the highest temperature for continuous using is about 120°C.
  • Coefficient of Linear Expansion: Polycarbonate is one of resin which has smaller coefficient of liner expansion.
  • Conductivity of Heat: There is no big difference between heat conductivity of Polycarbonate and other resin. It’s about 1/4 of Glass, 1/300 of Iron, 1/1000 of Aluminum, 1/12000 of Steel. Polycarbonate is a better material to keep warmth.
  • Temperature of Embrittlement: For embrittlement, Polycarbonate is lower than normal resin. It’s about -135°C, and the lowest temperature for continuous using is about -30°C.
  • Combustion: Polycarbonate is one of resin which gets burn not easily. During the process of heating up Polycarbonate, Polycarbonate would not produce toxic gas.
2. Property of Optics:
  • Weather Ability: When normal Polycarbonate panels are exposed outdoor for a long time, normal Polycarbonate panel become yellowish and crack on the surface. The surface of Polycarbonate panel, made by SUN ASIA, is all coating with Anti-UV material. As the results, the optic property and mechanical property would not have significant changes even under the exposure for a long time.
  • Diaphaneity: The diaphaneity of 1mm thickness clear Polycarbonate panel is above 85%, and the diaphaneity of 5mm thickness clear Polycarbonate panel is above 80%, similar with glass.
3. Mechanical Property:
  • Pull Resistance: Polycarbonate panel have better heat resistance. Even under 120°C, the pull resistance is still 350kgf/cm2.
  • Modulus of Bending Resistance: Polycarbonate panel have better bending resistance. Polycarbonate panel would not break, even if the angle is 80° ~ 90°.
4. Sound Insulation Property:
  • As the thickness is the same, the sound insulation property of Polycarbonate panels is better than glass under the high frequency.
5. Property of Weight:
  • At the same dimension, the weight of Polycarbonate board is half of glass. This can help us to save the cost of delivery and haul or construct more easily.
top


Technical Data

Characteristics Test Method Unit Polycarbonate Hollow Sheet Data Polycarbonate Solid Sheet Data
lzod Impact Strength (Notched) ASTM D256 kg • cm/cm (1/4") 15 14.3
Light Transmission ASTM D1003 % (3mm thick) 88 89
Specific Gravity ASTM D792 - 1.2 1.2
Coefficient of Linear Expansion ASTM D696 x10-5 cm/cm/°C 6 ~ 8 6 ~ 8
Service Temperature - °C -40°C ~ +120°C -40°C ~ +120°C
Thermal Conductivity ASTM C177 W/m°C 0.2 0.2
Tensile Strength ASTM D638 kg/cm² 630 630
Flexural Strength ASTM D790 kg/cm² 920 920
Flexural Modulus ASTM D790 kg • cm/cm(1/4") 24000 24000
Tensile Stress at Break ASTM D638 % 110 110
Rockwell Hardness ASTM D785 M Scale M-77 M-77
Heat Distortion Temperature ASTM D648 °C (4.6 Kg/cm², 120°C/hr) 136 136
Flammability UL 94 - 1.5mm V-2/HB 1.5mm V-2
top


Chemicals Incompatible to the PC Sheet

1. Acetic aldehyde 2. Strong acetic acid 3. Acetone 4. Acrylonitrile 5. Ammonia water
6. Ammonium fluoride sat'd 7. Ammonium chloride sat'd 8. Benzene 9. Benzoic acid 10. Benzyl alcohol
11. Brominated calcium nitrate 12. Carbolic acid 13. Carbon disulfide 14. Carbon tetrachloride 15. 5% potassium hydroxide solution
16. 5% sodium hydroxide solution 17. Chlorobenzene 18. Chloroform 19. Lilac 20. Cresol
21. Cyclohexanone 22. Cyclohexene 23. Dimethylformamide 24. Dioxin 25. Ethylamine
26. Ether 27. PVC 28. 2-Ethanolamine 29. 30% formic acid 30. Gasoline
31. Methacrylic acid methyl 32. Nitrobenzene 33. Nucleolus 34. Pyridine 35. Petroleum
36. Benzyl ethanol 37. Phenol 38. Chloroperoxide 39. Phosphorus trichloride 40. Styrene
41. Tetrachloroethane 42. THF 43. Tetralin 44. Thiophenes 45. Toluene
46. 10% trichloroamine 47. Xylene 48. Ammonium hydroxide 49. Chlorohydrocarbon 50. Ketone
51. Methyl-ethyl ketone 52. Dichloromethane 53. Ethylene hydroxide 54. Sodium hydroxide 55. Nitric acid
56. Cement 57. Oil      
top